Surface Integrity of Dimethacrylate Composite Resins with Low Shrinkage Comonomers.
Article in Materials (Basel, Switzerland), 2021. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 5 papers.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
5 citing papers in PubMed.
- Comparative Study of Direct Resin Composites with Different Formulations.Dentistry journal · 2026Article
- Characterization of temporary and permanent 3D-printed crown and bridge resins.Biomaterial investigations in dentistry · 2025Article
- Article
- Effect of different beverages and polishing techniques on colour stability of CAD/CAM composite restorative materials.Biomaterial investigations in dentistry · 2024Article
- A comparative assessment of color stability among various commercial resin composites.BMC oral health · 2023Article
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
5 authors.
Funding
No grant is acknowledged in the PubMed record.
Abstract
The goal of current research was to investigate the influence of adding low shrinkage "Phene" like comonomers hexaethylene glycol bis(carbamate-isoproply-α-methylstyrene) (HE-Phene) and triethylene glycol bis(carbamate-isoproply-α-methylstyrene) (TE-Phene) on the surface and color characteristics of composite resin. A range of weight fractions (0, 10, 20, 30, 40 wt.%) of HE/TE-Phene monomers were mixed with bisphenol A glycidyl methacrylate (GMA)/triethylene glycol dimethacrylate (TEGDMA) monomer. Experimental composite resins were made by mixing 71 wt.% of silica fillers to 29 wt.% of the resin matrix. A Vickers indenter and glossmeter were used for testing surface hardness (SH) and gloss (SG) at 60°. A chewing-simulator was used to evaluate the surface wear after 15,000 cycles. Color change (∆E) and translucency parameter (TP) were measured using a spectrophotometer. Data showed that HE/TE-Phene monomer had no negative impact (