Microwave irradiation coupled with zero-valent iron that enhances the composite geopolymerization of chromite ore processing residue and its mechanisms.

In this work, microwave (MW) irradiation was employed to enhance the zero-valent iron (ZVI)-dominated de-contamination of chromite ore processing residue (COPR). A coupling system and the traditional two-step procedure were both conducted to evaluate the effects of MW irradiation on the reduction and the incorporation of COPR into the composite materials-based geopolymers. The factors including the ratios of liquid to solid, the mass ratios of ZVI to COPR, and the acid dosage had some obvious influence on the reduction of COPR in the MW system. The compressive strengths of 31.54 and 41.56 MPa were determined from the two-step procedure and the coupling system at the COPR dosage of 10% (mass ratio), respectively. The employment of MW irradiation not only strengthened the formation of the geopolymer matrices but also improved the chemical stabilization of Cr species in the solidified blocks. The coupled process was more conducive to incorporating the treated COPR into the geopolymer-based crystalline microstructures compared with the subsequent usage of ZVI reduction and MW irradiation.