Systemically delivered antibody-labeled magnetic iron oxide nanoparticles are less toxic than plain nanoparticles when activated by alternating magnetic fields.

objectiveToxicity from off-target heating with magnetic hyperthermia (MHT) is generally assumed to be understood. MHT research focuses on development of more potent heating magnetic iron oxide nanoparticles (MIONs), yet our understanding of factors that define biodistribution following systemic delivery remains limited. Preclinical development relies on mouse models, thus understanding off-target heating with MHT in mice provides critical knowledge for clinical development.

methodsEight-week old female nude mice received a single tail vein injection of bionized nanoferrite (BNF) MIONs or a counterpart labeled with a polyclonal human antibody (BNF-IgG) at 1 mg, 3 mg or 5 mg Fe/mouse on day 1. On day 3, mice were exposed to an alternating magnetic field (AMF) having amplitude of 32, 48 or 64 kA/m at ∼145 kHz for 20 min. Twenty-four hours later, blood, livers and spleens were harvested and analyzed.

resultsDamage to livers was apparent by histology and serum liver enzymes following MHT with BNF or BNF-IgG at doses ≥3 mg Fe and AMF amplitudes ≥48 kA/m. Differences between effects with BNF vs. BNF-IgG at a dose of 3 mg Fe were noted in all measures, with less damage and increased survival occurring in mice injected with BNF-IgG. Necropsies revealed severe damage to duodenum and upper small intestines, likely the immediate cause of death at the highest MHT doses.

conclusionResults demonstrate that the MION coating affects biodistribution, which in turn determines off-target effects. Developments to improve heating capabilities of MIONs may be clinically irrelevant without better control of biodistribution.