Preparation of collagen/cellulose nanocrystals composite films and their potential applications in corneal repair.

As the main component of the natural cornea, collagen (COL) has been widely applied to the construction of corneal repair materials. However, the applications of collagen are limited due to its poor mechanical properties. Cellulose nanocrystals (CNCs) possess excellent mechanical properties, optical transparency and good biocompatibility. Therefore, in this study, we attempted to introduce cellulose nanocrystals into collagen-based films to obtain corneal repair materials with a high strength. CNCs were incorporated at 1, 3, 5, 7 and 10 wt%. The physical properties of these composite films were characterized, and in vitro cell-based analyses were also performed. The COL/CNC films possessed better mechanic properties, and the introduction of CNCs did not affect the water content and light transmittance. The COL/CNC films demonstrated good biocompatibility toward rabbit corneal epithelial cells and keratocytes in vitro. Moreover, the collagen films with appropriate ration of CNCs effectively induced the migration of corneal epithelial cells and inhibited the myofibroblast differentiation of keratocytes. A collagen film with 7 wt% CNCs displayed the best combination of physical properties and biological performance in vitro among all the films. This study describes a nonchemical cross-linking method to enhance the mechanical properties of collagen for use in corneal repair materials and highlights potential application in corneal tissue engineering.