ArticleMaterials (Basel, Switzerland)2019
Fracture Characteristics and Analysis in Dissimilar Cu-Al Alloy Joints Formed via Electromagnetic Pulse Welding.
Article in Materials (Basel, Switzerland), 2019. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 1 paper.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
1 citing paper in PubMed.
- Friction Stir Spot Welding of Aluminum and Copper: A Review.Materials (Basel, Switzerland) · 2019Review
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors.
Funding
Abstract
The aim of this study was to identify and analyze the fatigue fracture characteristics of dissimilar Al 6061 to Cu (UNS C11000) lap joints made with ultrafast electromagnetic pulse welding (EMPW) via fractography, stress analysis and finite element simulation. It was observed that EMPW generated an annular (or ring-shaped) bonding area, with weld zones and a central non-weld zone when viewed from the cross section. Two types of failure modes occurred in relation to the cyclic loading levels: base metal fracture or transverse through-thickness (TTT) crack growth at a higher loading level, and joint interfacial failure at a lower loading level. In the interfacial failure, fatigue crack initiated from the outer edge of annular welding area, and propagated to form an approximate elliptical boundary. Fatigue crack propagation was characterized by fatigue striations existing in discrete areas on the fracture surface. This was attributed to a coupled role of shear and normal stresses present in a tensile lap shear sample due to the bending moment caused by the inherent misalignment. The final rapid fracture started from elliptical boundary with elongated shear dimples. Both theoretical stress analysis and finite element model revealed the maximum stress and stress concentration along the outer edge, where fatigue crack initiation occurred.