Rheological Behavior of Amino-Functionalized Multi-Walled Carbon Nanotube/Polyacrylonitrile Concentrated Solutions and Crystal Structure of Composite Fibers.

The rheological behavior of amino-functionalized multi-walled carbon nanotubes (amino-CNTs)/polyacrylonitrile (PAN) concentrated solutions in the dimethyl sulphoxide solvent and the effects of the amino-CNTs on the PAN precursor fibers by wet-spinning method were investigated. The amino-CNT/PAN concentrated solutions prepared by in situ solution polymerization with homogeneous dispersion of amino-CNTs have higher complex viscosity, storage modulus and loss modulus as compared to the control PAN concentrated solutions containing 22% PAN polymer by mass. The composite fibers with amino-CNTs of 1 wt % have lower degree of crystallization, crystal size and crystal region orientation compared to the control PAN precursor fibers. However, the amino-CNT/PAN composite fibers with diameter of about 10.5 μm exhibit higher mechanical properties than the control PAN precursor fibers with diameter of about 8.0 μm. Differential scanning calorimetry analysis demonstrated that the cyclization reaction in composite fibers have broad exothermic temperature range and low exothermic rate. These results indicate that the addition of amino-CNTs into PAN precursor fibers is beneficial to controlling the process of thermal stabilization and obtaining the higher performance of composite fibers.