ArticleLasers in medical science2019
Push-out bond strength of calcium-silicate cements following Er:YAG and diode laser irradiation of root dentin.
Article in Lasers in medical science, 2019. The graph could read no effect estimate from its abstract, so it casts no vote on the map. Cited by 7 papers, 1 of them a synthesis that pooled it.
What it found
Each row is one number read from the abstract, on the scale the paper reported it, with its interval. Left of the dashed line favours the treatment, right favours the comparator. Under each row is the sentence it came from. New to these charts? A ten-minute tutorial.
The abstract states no effect estimate the extractor could read, or names no intervention and outcome on the map, so this paper lights no cell and moves no belief. It is still indexed, cited and linked below.
The trial behind it
Trials whose registry record cites this paper, or whose number appears in the abstract. A trial that started after this paper was published is citing it as background, not reporting it.
Neither the registry nor the abstract names a trial number. If this is a trial report, that itself is worth knowing.
Who cites it
7 citing papers in PubMed, 1 synthesis or guideline pooled it, 12 citations in OpenAlex.
- Comprehensive review of composition, properties, clinical applications, and future perspectives of calcium-enriched mixture (CEM) cement: a systematic analysis.Biomedical engineering online · 2024Pooled it
- The Effect of Dentin Exposure to Various Gutta-Percha Solvents on the Bond Strength of Calcium-Enriched Mixture Cement.International journal of dentistry · 2026Article
- Effect of Incorporating Titanium Dioxide Nanoparticles into White Portland Cement, White Mineral Trioxide Aggregate, and Calcium Enriched Mixture Cement on the Push-out Bond Strength to Furcal Area Dentin.Journal of dentistry (Shiraz, Iran) · 2023Article
- Different Dentin Conditioning Protocols on Bond Strength of a Bioceramic Root Canal Filling.Acta stomatologica Croatica · 2023Article
- Push-out bond strength of two calcium silicate-based cements used for repair of artificial furcal perforation following different power outputs of Nd:YAG laser.Lasers in medical science · 2022Article
- Efficacy of Photoinduced Photoacoustic Streaming and Diode Laser Irrigation Techniques on Smear Layer Removal, Sealer Penetration and Push-out Bond Strength.Journal of lasers in medical sciences · 2022Article
- Effect of blood contamination and various hemostatic procedures on the push-out bond strength of Biodentine when used for furcation perforation repair.Journal of conservative dentistry : JCDArticle
Corrections and comments
PubMed lists nothing against this paper. Absence here is not a guarantee, only a check that was made.
Authors and funding
6 authors at 2 institutions in 1 country.
Funding
Abstract
This study aimed to compare the effects of diode and Er:YAG laser irradiation of root dentin on push-out bond strength of mineral trioxide aggregate (MTA) and calcium-enriched mixture (CEM) cements. An in vitro experimental study was conducted on 90 dentin discs, cut out of freshly extracted human teeth. The discs were instrumented to obtain 1.3-mm lumen diameter. Then, they were randomly divided into six groups (n = 15). Groups 1 and 4 subjected to diode laser (Wiser, Doctor Smile, Italy) (980 nm, 1 W, continuous mode) for 10 s and filled with MTA and CEM cements. Groups 2 and 5 subjected to Er:YAG laser (Deka, Italy) (2940 nm, 1 W, 10 Hz, 230 μs) for 10 s and filled with MTA and CEM cements. Groups 3 and 6 (control groups) were filled with MTA and CEM cements without laser irradiation. After 7 days, push-out bond strength test was performed using a universal testing machine in order to evaluate the adhesion of the biomaterials to dentin. The samples were evaluated under a light microscope at × 40 magnification to determine the mode of fracture. Data were analyzed using two-way ANOVA. The highest push-out bond strength (8.76 ± 3.62 MPa) was noted in group 1 (diode/MTA), which was significantly higher than the other groups (P < 0.001). The lowest bond strength (2.61 ± 0.81) was noted in group 6 (control/CEM). Diode laser significantly increased the bond strength of both cements (P < 0.05), but Er:YAG laser irradiation only increased the bond strength of CEM and had no significant effect on MTA (P = 0.603). The bond strength of MTA control group was higher than that of CEM control group (P = 0.001). Push-out bond strength of endodontic cements can be affected by dentin conditioning with diode 980 nm and Er:YAG laser. Nine hundred eighty-nanometer diode laser irradiation is recommended to increase the bond strength of endodontic cements particularly the CEM cement to dentin.