Suggested Procedures for the Reproducible Synthesis of Poly(d,l-lactide-co-glycolide) Nanoparticles Using the Emulsification Solvent Diffusion Platform.

backgroundPoly(d,l-lactide-co-glycolide) (PLGA) based biodegradable nanoparticles are of key interest for the development of controlled release drug delivery systems and for other biomedical applications. It has been reported that PLGA polymers can be converted into colloidal nanoparticulate systems by various techniques, such as emulsification-diffusion, emulsification-evaporation, interfacial deposition, salting out, dialysis and nanoprecipitation. Emulsification-evaporation with water immisci-ble solvents including dichloromethane and chloroform has been the preferred method for the synthesis of PLGA nanoparticles due to the low boiling point and limited water solubility of these solvents. We and others, however, have found that when water-immiscible solvents are used for the synthesis of PLGA nanoparticles, particle aggregation, non-uniform particle size and multimodal size distribution are commonly encountered problems. This suggests that the synthesis of PLGA nanoparticles using water immiscible solvents is highly sensitive to small procedural variations that affect overall reproduc-ibility.

objectiveThis study presents a simple and robust procedure for the preparation of PLGA nanoparti-cles with very small batch to batch variability (<5% variability in size (z-average) as determined by dynamic light scattering).

resultsThe results showed that the emulsification solvent diffusion method teamed with partially water-miscible solvents, such as ethyl acetate, is a versatile approach for the preparation of PLGA na-noparticles with highly reproducible sizes (between 50 and 400 nm) and zeta potentials (between -30 and +30 mV), with relatively narrow polydispersity.

conclusionEmulsification-diffusion with ethyl acetate is, therefore, a more reliable alternative to sev-eral existing procedures for the reproducible and refined synthesis of PLGA nanoparticles.