[Effect of silk fibroin/poly (

Objective: To explore the effect of silk fibroin/poly( Methods: SF/P(LLA-CL) nanofibrous scaffold was fabricated by electrospinning methods. The morphology of the scaffold was observed by scanning electron microscope (SEM). Pre-osteoblasts MC3T3-E1 cells were seeded on the scaffold and cultured for 1, 3, and 5 days. Cell adhesion and proliferation were also observed by SEM. Meanwhile, twenty-four New Zealand white rabbits were randomly divided into the autogenous tendon group (control group) and the autogenous tendon wrapped with SF/P(LLA-CL) scaffold group (experimental group), with twelve rabbits in each group. An extra-articular model was established, the effect was evaluated by histological examination and mechanical testing. Results: The morphology of SF/P(LLA-CL) nanofibrous scaffold was random, with a diameter of (219.4±66.5) nm. SEM showed that the MC3T3-E1 cells seeded on the scaffold were in the normal shape, growing well, and proliferating with time course. The results of histological examination showed that inflammatory cells infltrated into the graft-host bone interface at 6 weeks after operation in both groups. Besides, the width of interface showed no significant difference between groups. At 12 weeks after operation, protruding new bone tissue could be observed at the interface in the experimental group, while scar tissue but no new bone tissue could be seen at the interface in the control group. Mechanical testing showed that there was no significant difference in the failure load and the stiffness between groups at 6 weeks after operation ( Conclusion: The SF/P(LLA-CL) nanofibrous scaffold has good cell biocompatibility and can effectively promote tendon-bone healing, thus providing new method for modifying graft for ACL reconstruction in the clinical practice.