Electrochemical aptasensor for endocrine disrupting 17β-estradiol based on a poly(3,4-ethylenedioxylthiopene)-gold nanocomposite platform.

A simple and highly sensitive electrochemical DNA aptasensor with high affinity for endocrine disrupting 17β-estradiol, was developed. Poly(3,4-ethylenedioxylthiophene) (PEDOT) doped with gold nanoparticles (AuNPs) was electrochemically synthesized and employed for the immobilization of biotinylated aptamer towards the detection of the target. The diffusion coefficient of the nanocomposite was 6.50 × 10(-7) cm(2) s(-1), which showed that the nanocomposite was highly conducting. Electrochemical impedance investigation also revealed the catalytic properties of the nanocomposite with an exchange current value of 2.16 × 10(-4) A, compared to 2.14 × 10(-5) A obtained for the bare electrode. Streptavidin was covalently attached to the platform using carbodiimide chemistry and the aptamer immobilized via streptavidin-biotin interaction. The electrochemical signal generated from the aptamer-target molecule interaction was monitored electrochemically using cyclic voltammetry and square wave voltammetry in the presence of [Fe(CN)(6)](-3/-4) as a redox probe. The signal observed shows a current decrease due to interference of the bound 17β-estradiol. The current drop was proportional to the concentration of 17β-estradiol. The PEDOT/AuNP platform exhibited high electroactivity, with increased peak current. The platform was found suitable for the immobilization of the DNAaptamer. The aptasensor was able to distinguish 17β-estradiol from structurally similar endocrine disrupting chemicals denoting its specificity to 17β-estradiol. The detectable concentration range of the 17β-estradiol was 0.1 nM-100 nM, with a detection limit of 0.02 nM.