Pseudoxanthomonas bacteria that drive deposit formation of wood extractives can be flocculated by cationic polyelectrolytes.

Runnability problems caused by suspended bacteria in water using industries, have, in contrast to biofilms, received little attention. We describe here that Pseudoxanthomonas taiwanensis, a wide-spread and abundant bacterium in paper machine water circuits, aggregated dispersions of wood extractives ("pitch") and resin acid, under conditions prevailing in machine water circuits (10(9) cfu ml(-1), pH 8, 45°C). The aggregates were large enough (up to 50 μm) so that they could be expected to clog wires and felts and to reduce dewatering of the fiber web. The Pseudoxanthomonas bacteria were negatively charged over a pH range of 3.2-10. Cationic polyelectrolytes of the types used as retention aids or fixatives to flocculate "anionic trash" in paper machines were effective in flocculating the Pseudoxanthomonas bacteria. The polyelectrolyte most effective for this purpose was of high molecular weight (7-8 × 10(6) g mol(-1)) and low charge density (1 meq g(-1)), whereas polyelectrolytes that effectively zeroed the electrophoretic mobility (i.e., neutralized the negative charge) of the bacterium were less effective in flocculating the bacteria. Based on the results, we concluded that the polyelectrolytes functioning by bridging mechanism, rather than by neutralization of the negative charge, may be useful as tools for reducing harmful deposits resulting from interaction of bacteria with wood extractives in warm water industry.